Name: Invar 36 Nickel Iron Alloy Tubes with High Dimensional Stability and Corrosion Resistance for Precision Instruments
Brand: Shanghai Tankii Alloy Material Co.,Ltd
SKU: invar36
Price: 499.05 USD
Availability: InStock

Produkt-Details

Herkunftsort: Shanghai, China

Markenname: TANKII

Zertifizierung: ISO9001, SGS

Modellnummer: invar36

Zahlungs-u. Verschiffen-Ausdrücke

Min Bestellmenge: 10 kg

Preis: Verhandlungsfähig

Verpackung Informationen: Holzkiste

Lieferzeit: 7-20 Tage

Zahlungsbedingungen: L/C, T/T, Western Union

Versorgungsmaterial-Fähigkeit: 100 Tonnen pro Monat

Erhalten Sie besten Preis

Kontaktieren Sie uns jetzt

Spezifikationen

Beschreibung

Spezifikationen

Hervorheben: 
                                                                                                                                                                                                                                                                                                                                                                                                                                                          Invar 36 nickel iron alloy tubes, Invar36 pipes for green buildings, precision alloy Invar 36 tubes
                                                  

Modell Nr.:	Invar 36	OD:	0,20 mm min
WT:	0.015 mm	Länge:	0,20 mm min.
Form:	Spulenrohr; Kapillarrohr Nahtlose Rohre	Oberfläche:	Helle Oberfläche
Probe:	kleiner Auftrag angenommen

Modell Nr.:	Invar 36
OD:	0,20 mm min
WT:	0.015 mm
Länge:	0,20 mm min.
Form:	Spulenrohr; Kapillarrohr Nahtlose Rohre
Oberfläche:	Helle Oberfläche
Probe:	kleiner Auftrag angenommen

Beschreibung

Invar 36 Nickel Iron Alloy Tubes with High Dimensional Stability and Corrosion Resistance for Precision Instruments

4J36 (Invar) is used where high dimensional stability is required, such as precision instruments, clocks, seismic creep gauges, television shadow-mask frames, valves in motors, and antimagnetic watches. In land surveying, when first-order (high-precision) elevation leveling is to be performed, the Level staff (leveling rod) used is made of Invar, instead of wood, fiberglass, or other metals. Invar struts were used in some pistons to limit their thermal expansion inside their cylinders.

4J36 use oxyacetylene welding, electric arc welding, welding and other welding methods. Since the coefficient of expansion and chemical composition of the alloy is related should be avoided due to welding causes a change in the alloy composition, it is preferable to use Argon arc welding welding filler metals preferably contains 0.5% to 1.5% titanium, in order to reduce weld porosity and crack.

Normal composition%

Ni	35~37.0	Fe	Bal.	Co	-	Si	≤0.3
Mo	-	Cu	-	Cr	-	Mn	0.2~0.6
C	≤0.05	P	≤0.02	S	≤0.02

Coefficient of expansion

θ/ºC	α1/10-6ºC-1	θ/ºC	α1/10-6ºC-1
20~-60	1.8	20~250	3.6
20~-40	1.8	20~300	5.2
20~-20	1.6	20~350	6.5
20~-0	1.6	20~400	7.8
20~50	1.1	20~450	8.9
20~100	1.4	20~500	9.7
20~150	1.9	20~550	10.4
20~200	2.5	20~600	11.0

The heat treatment process
Annealing for stress relief	Heated to 530~550ºC and hold 1~2 h. Cold down
annealing	In order to eliminate hardening, which be bring out in cold-rolled, cold drawing process. Annealing needs heated to 830~880ºC in vacuum,hold 30 min.
The stabilization process	In protective media and heated to 830 ºC, hold 20min. ~ 1h, quench Due to the stress generated by quenching, heated to 315ºC,hold 1~4h.
Precautions	Can not be hardened by heat treatment Surface treatment can be sandblasting, polishing or pickling. Alloy can be used 25% hydrochloric acid pickling solution at 70 ºC to clear oxidized surface

Typical Physical properties

Density (g/cm3)	8.1
Electrical resistivity at 20ºC(OMmm2/m)	0.78
Temperature factor of resistivity(20ºC~200ºC)X10-6/ºC	3.7~3.9
*Thermal conductivity, λ/ W/(mºC)**	11
Curie point Tc/ ºC	230
Elastic Modulus, E/ Gpa	144

Invar 36 Nickel Iron Alloy Tubes with High Dimensional Stability and Corrosion Resistance for Precision Instruments 0

Tags:

Platin-Iridium-Legierungsrohr mit hoher Korrosionsbeständigkeit und 0,2 mm min. Außendurchmesser für biokompatible medizinische Anwendungen

Erhalten Sie besten Preis

Pt90Ir10 Platin-Iridium-Legierungsturb mit 0,2 mm Min. Durchmesser und hellen Aufgelösten Oberfläche für medizinische Katheter

Erhalten Sie besten Preis

Schicken Sie uns Ihren Antrag bitte und wir antworten auf Sie so bald wie möglich.

Senden Sie

Kupfer Nickel Alloy Wire

Elektrischer Widerstand-Draht

Thermoelement-bloßer Draht

Fecral-Legierung

Thermoelementleitung

Nicr-Legierung

Thermischer Spray-Draht

Ofen-Heizelement

Präzisions-Legierung

Kupferlegierung

Nickellegierung

Emaillierter Draht

Hochtemperaturlegierung

Thermoelement-Verbindungsstück

Invar 36 Nickel Iron Alloy Tubes with High Dimensional Stability and Corrosion Resistance for Precision Instruments