Fecral resistohm145 A1 D A1 Tk1 APM High-Temperature Heating Wire

Name: Fecral resistohm145 A1 D A1 Tk1 APM High-Temperature Heating Wire
Brand: Shanghai Tankii Alloy Material Co.,Ltd
SKU: TK APM
Price: 35.00 USD
Availability: InStock

Produkt-Details

Place of Origin: Shanghai

Markenname: TANKII

Zertifizierung: ISO

Model Number: TK APM

Zahlungs-u. Verschiffen-Ausdrücke

Minimum Order Quantity: 10 KG

Preis: Verhandlungsfähig

Packaging Details: wooden Case

Delivery Time: 10-25 day

Payment Terms: L/C,T/T,Western Union,MoneyGram,D/P,D/A

Supply Ability: 100　Tons/Month

Erhalten Sie besten Preis

Kontaktieren Sie uns jetzt

Spezifikationen

Beschreibung

Spezifikationen

Hervorheben:

Material:	FECRAL ALLOY	Resistivity:	1.45
Density:	7.1 g/cm3	surface:	Bright， Golden， Oxitation，blue etc.
Shape:	flat wire, ribbon, round wire, bar,rod, pipe tube,	HS Code:	72230000
sample:	accepted	diameter:	0.05-10.00 mm

Material:	FECRAL ALLOY
Resistivity:	1.45
Density:	7.1 g/cm3
surface:	Bright， Golden， Oxitation，blue etc.
Shape:	flat wire, ribbon, round wire, bar,rod, pipe tube,
HS Code:	72230000
sample:	accepted
diameter:	0.05-10.00 mm

Beschreibung

Fecral resistohm145 A1 D A1 Tk1 APM High-Temperature Heating Wire

TK APM Tubes are an advanced powder metallurgical, dispersion strengthened, ferritic iron-chromium-aluminium alloy (FeCrAl alloy) for use at tube temperatures up to 1250°C (2280°F).

TK APM tubes have good form stability at high temperature. TK APM forms an excellent, non-scaling surface oxide, which gives good protection in most furnace environments, i.e. oxidizing, sulphurous and carburizing, as well as against deposits of carbon, ash, etc. The combination of excellent oxidation properties and form stability makes the alloy unique.

Typical applications for TK APM are as radiant tubes in electrically or gas fired furnaces such as continuous galvanizing furnaces, seal quench furnaces, holding furnaces and dosing furnaces in the aluminium, zinc, lead industries, thermocouple protection tubes, furnace muffles for sintering applications.

Composition(Wt%)

	C	Si	Mn	Cr	Al	Fe
Min	-	-	-	20	5.5	Bal.
Max	0.04	0.5	0.4	22	6.0	Bal.

Mechanical Properties

Tensile Strength at Room Temperature	650 - 750 MPa
Elongation Rate	15 -25%
Hardness	220 - 260 HV
Tensile Strength at 1000℃	22 - 27 MPa
High Temperature Durability at 1000℃ and 6MPa	≥100 h

Physical Properties

Density	7.10 g/cm³
Resistivity	1.45×10^-6 Ω.m
Melting Point	1500 ℃
Maximum Continuous Working Temperature	1400 ℃
Resistance Temperature Coefficient(Ct)	800℃	1000℃	1400℃
Resistance Temperature Coefficient(Ct)	1.03	1.04	1.05
Average Linear Expansion Coefficient	20-800℃	20-1000℃	20-1400℃
Average Linear Expansion Coefficient	14	15	16

Fast life

1300℃

1350℃

Average Fast Life (Hours)

110

Sagging Rate After Rupture

Fecral resistohm145 A1 D A1 Tk1 APM High-Temperature Heating Wire 0

Specifications

Wire diameter range φ0.1-10mm

Tags:

Schicken Sie uns Ihren Antrag bitte und wir antworten auf Sie so bald wie möglich.

Senden Sie

Kupfer Nickel Alloy Wire

Elektrischer Widerstand-Draht

Thermoelement-bloßer Draht

Fecral-Legierung

Thermoelementleitung

Nicr-Legierung

Thermischer Spray-Draht

Ofen-Heizelement

Präzisions-Legierung

Kupferlegierung

Nickellegierung

Emaillierter Draht

Hochtemperaturlegierung

Thermoelement-Verbindungsstück

Fecral resistohm145 A1 D A1 Tk1 APM High-Temperature Heating Wire

Legierung des Kupfers und des Nickels,

Kupferlegierung des Nickels,

Kupfer- und Nickellegierung

Gutes Korrosionsbeständigkeit Monel Rohr/Rohr des kupfernes Nickel-Legierungs-Draht-400 für Kühlturm

Mangan-kupferner elektrischer beständiger Draht-gute Stabilität für Emitter-Widerstand